TE Connectivity Expandable Cross Linked Elastomer Black Cable Sleeve, 12 (Supplied) mm, 6 (After Recovery) mm Diameter,

Номер на артикул на RS: 182-5606Марка: TE Connectivity№ по каталога на производителя: EK8088-000
brand-logo
Преглед на всички в Кабелни ръкави

Технически документи

Спецификации

Brand

TE Connectivity

Sleeve Diameter

12 (Supplied) mm, 6 (After Recovery) mm

Colour

Black

Material

Cross Linked Elastomer

Sleeve Length

8m

Expandable

Yes

Minimum Cable Diameter

6mm

Maximum Cable Diameter

12mm

Minimum Operating Temperature

-75°C

Maximum Operating Temperature

+150°C

Fire Behaviour

Flame Retardant, Halogen Free

Dielectric Strength

14kV/mm

Wall Thickness

0.9mm

Series

ZH150

Shrink Ratio

2:1

Страна на произход

Czech Republic

Информацията за складовите наличности временно не е налична.

Моля, проверете отново по-късно.

Информацията за складовите наличности временно не е налична.

P.O.A.

TE Connectivity Expandable Cross Linked Elastomer Black Cable Sleeve, 12 (Supplied) mm, 6 (After Recovery) mm Diameter,

8

Предлагат се на бройка по 8
8P.O.A.
16P.O.A.
24P.O.A.
32P.O.A.
40P.O.A.
48P.O.A.
56P.O.A.
64P.O.A.
72P.O.A.
80P.O.A.
88P.O.A.
96P.O.A.
104P.O.A.
112P.O.A.
120P.O.A.

P.O.A.

TE Connectivity Expandable Cross Linked Elastomer Black Cable Sleeve, 12 (Supplied) mm, 6 (After Recovery) mm Diameter,
Информацията за складовите наличности временно не е налична.

8

Предлагат се на бройка по 8
8P.O.A.
16P.O.A.
24P.O.A.
32P.O.A.
40P.O.A.
48P.O.A.
56P.O.A.
64P.O.A.
72P.O.A.
80P.O.A.
88P.O.A.
96P.O.A.
104P.O.A.
112P.O.A.
120P.O.A.

Технически документи

Спецификации

Brand

TE Connectivity

Sleeve Diameter

12 (Supplied) mm, 6 (After Recovery) mm

Colour

Black

Material

Cross Linked Elastomer

Sleeve Length

8m

Expandable

Yes

Minimum Cable Diameter

6mm

Maximum Cable Diameter

12mm

Minimum Operating Temperature

-75°C

Maximum Operating Temperature

+150°C

Fire Behaviour

Flame Retardant, Halogen Free

Dielectric Strength

14kV/mm

Wall Thickness

0.9mm

Series

ZH150

Shrink Ratio

2:1

Страна на произход

Czech Republic